PU Pigmented Finishes

01. PU White Matt (OPP530NI)

This is a series of high quality topcoats, characterized by high covering power and surface durability. It has excellent resistance to yellowing (due to the presence of uv filter) in a combination with hardener cth3. Especially formulated for high quality pigmented systems, suitable for kitchens and furniture in general. The white base opp530ni and the referred transparent binder cr4500g series can be tinted with pu pigmented ppp30 pastes series, in order to achieve a huge range of different colours.

PHYSICAL AND CHEMICAL PROPERTIES

PROPERTIES
Specific weight: 1,36 ± 0,01 kg (g/cc at 20°C)
Viscosity: (DIN cup 4 at 20°C) 150” ± 5”
Solid content: 65 ± 1%.

APPLICATION METHOD
By spray and curtain coater

SPECIFICS

PREPARATION

OPP530NI series 100 parts
by weight
CTH3 50 parts by weight
(non yellowing)
DPU809 50 parts by weight

EXPENDITURE
100-150 g/sm on one layer

DRYNG TIME
DRYING at 20°C:
• Flash off in 20-25 minutes;
• Touch dry in 45-60 minutes;
• Stackable minimum in 12 hours

STORAGE
Keep in a fresh and well ventilated place; do not exceed 25°-28° C. Polyisocianic catalysts should always be kept dry; in the event of partial use close the tins again perfectly and use the remaining product in a short period of time.

02. PU White Sealer (FPP225TIX)

This is a white thixotropic polyurethane primer applicable by spray. Among its main characteristics, there are good covering power, verticality, uniformity, very good sandability and a good white point.

PHYSICAL AND CHEMICAL PROPERTIES

PROPERTIES
Specific weight: 1,42 ± 0,01 kg/l (g/cc at 20°C)
Viscosity: (DIN Ø 4 20°C) 70” ± 5
Solid content: 71 ± 1%

APPLICATION METHOD
By spray

SPECIFICS

PREPARATION

FPP225TIX 100 parts by weight
CT7 50 parts by weight – General use
DPU809 50 parts by weight

EXPENDITURE
80-130 g/sm on one or two layers

DRYNG TIME
• Flash off in 15 minutes;
• Touch dry in 30-40 minutes;
• Stacking in 12 hours minimum

STORAGE

Keep in a fresh and well ventilated places; do not exceed 25°-28°C. Polyisocianic catalysts should always be kept dry; if partially used, re-seal the packs perfectly and use up the remaining product within a short period of time.

03. PU White Gloss (LPP2530NC)

It’s a pigmented high gloss topcoats series with fast drying time, very good filling power, smoothness and surface hardness. Excellent the yellowing resistance. Suitable for buffing. The white base lpp2530nc and the referred transparent binder cr4072 can be tinted with pu pigmented ppp30 pastes series, in order to achieve a huge range of different colours.

PHYSICAL AND CHEMICAL PROPERTIES

PROPERTIES
Specific weight: 1,38 ± 0,01 (g/cc at 20°C)
Viscosity: (DIN Ø 4 20°C) 140” ± 5”
Solid content: 72 ± 1%

APPLICATION METHOD
By spray and curtain coater

SPECIFICS

PREPARATION

LPP2530NC series
100 parts by weight
CTH46 100 parts by weight or
CTH3 100 parts by weight
DPU809 40 parts by weight

EXPENDITURE
120-150 g/sqm on one or two coats

STORAGE
Store in cool, well ventilated places. The components react with atmospheric moisture. Keep the partially used packaging tightly closed. The storage period is 12 months in original sealed packs.

SUGGESTED CYCLE
• PCV2090/AP2/CP2/LZC1000 – 100:2:2
mixing ratio – 200-250 g/sqm
• PCV2090/AP2/CP2/LZC1000 – 100:2:2
mixing ratio – 200-250 g/sqm
• Sanding after overnight
• LPP2530NC series/CTH46/DPU809 – 2:2:1
mixing ratio – 150-160 g/sqm
• Buffing after 48-72 hours
• Stacking after 48 hours

04. PU White Gloss Eco (LPP030)

A white polyurethane high gloss topcoat endowed with excellent levelling, optimal final gloss level and covering power. Good surface hardness and yellowing resistance. It can be easily applied both by spray and curtain coater, especially on sanded polyester primer. This product can be properly tinted with fbu series of universal pastes.

PHYSICAL AND CHEMICAL PROPERTIES

PROPERTIES
Specific weight: 1,35 ± 0,01 (g/cc at 20°C)
Viscosity: (DIN Ø 4 20°C) 140” ± 5”
Solid content: 72 ± 1%

APPLICATION METHOD
By spray and curtain coater

SPECIFICS

PREPARATION

LPP030 series
100 parts by weight
CTH46 50 parts by weight
DPU809 50 parts by weight

EXPENDITURE
120-150 g/sqm on one or two coats

STORAGE

Store in cool, well ventilated places. The components react with atmospheric moisture. Keep the partially used packaging tightly closed. The storage period is 12 months in original sealed packs.

SUGGESTED CYCLE
• PCV2090/AP2/CP2/LZC1000 – 100:2:2
mixing ratio – 200-250 g/sqm
• PCV2090/AP2/CP2/LZC1000 – 100:2:2
mixing ratio – 200-250 g/sqm
• Sanding after overnight
• LPP2530NC series/CTH46/DPU809 – 2:2:1
mixing ratio – 150-160 g/sqm
• Buffing after 48-72 hours
• Stacking after 48 hours