Sirca

Wood Coatings (ITALY)

Home PU Clear Finishes

PU Clear Finishes

01.Epoxy (ISOLATE)

This is a primer for exotic woods and hardwood. It is suitable also to be used on mdf of poor quality to improve the adhesion.It’s possible to achieve special effects choosing properly the clear binder and the thinner.

PHYSICAL AND CHEMICAL PROPERTIES

PROPERTIES

Specific weight: 0,91 ± 0,01 (g/cc at 20°C)
Viscosity: 18”± 2 (DIN 4 at 20°C)
Solid content: 18 ± 1%

APPLICATION METHOD

Spray and curtain coater

SPECIFICS

PREPARATION

FPI35S06 100 parts by weight;
CT20 100 parts by weight
DPU809 30 – 50 parts by weight

EXPENDITURE
70 – 120 g/sm on one layer. If two layers are needed, wait 60-90
minutes before the second one.

DRYNG TIME
DRYING: at 20°C:
• Dust free in 20 minutes
• Touch dry in 40 minutes
Overcoatable after 90 minutes without sanding. After six hours a light sanding is needed

STORAGE
Store in cool, well ventilated places. The components react with
atmospheric moisture. After using, please close the can properly. The storage period is 12 months in original sealed packaging.

 

02.PU Clear Sealer (FPU15S01)

This is a universal polyurethane selaer, characterised by high transparency, good general properties and coverage.

It is suitable for painting doors for interior, accessories and furniture in general.

PHYSICAL AND CHEMICAL PROPERTIES

PROPERTIES

Specific weight: 0,98 ± 0,01 g/cc at 20°C
Viscosity: (DIN Ø 4 20°C) 35” ± 5
Solid content: 43 ± 1%

APPLICATION METHOD

​By spray

SPECIFICS

PREPARATION

FPU15S01 100 parts by weight;
CT23NOR 50 parts by weight;
DPU809 30-50 parts by weight

EXPENDITURE
80-140 g/sm in one, two or three coats

DRYNG TIME

DRYING: at 20°C:
• Flash off 20 – 25 minutes;
• Touch dry 45 – 50 minutes;
• Stacking in 12 hours minimum.

STORAGE
Keep in a fresh and well ventilated places; do not exceed 25°-28°C. Polyisocianic catalysts should always be kept dry; if partially used, re-seal the packaging perfectly and use the remaining product within a short period of time.

 

03.PU Clear Sealer (FPU18)

This is a polyurethane primer with good general characteristics and a quite high viscosity, which allows it also to be applied vertically on accessories (small wooden parts, etc.) and assembled furniture. It cures quickly and sands very well.

PHYSICAL AND CHEMICAL PROPERTIES

PROPERTIES

Specific weight : 0.95 ± 0.01 (g/cc at 20° C) Solid content : 46% ± 1 Viscosity: (DIN Ø 4 20°C) 50″ ± 5″

APPLICATION METHOD

​By Spray

SPECIFICS

PREPARATION

FPU18 100 parts in weight
CT23 50 parts by weight
DPU809 20-30 parts by weight

EXPENDITURE
80-150 g/sm on one or two coats

DRYNG TIME
DRYING: at 20°C:
• Dust free in 25 minutes;
• Touch dry in 45 minutes;
• Stackable in 12 hours
• Sandable in 4 hours

STORAGE
Keep in a fresh and well ventilated place; do not exceed 25°-28° C. Polyisocianic catalysts should always be kept dry; in the event of partial use close the tins again perfectly and use the remaining product in a short period of time.

 

04. PU Clear Matt (OPU77S15G/20/30/50/70)

This universal topcoat series has excellent covering power, it gives a good surface hardness, homogeneity, and smoothness. It is characterized by high resistance towards chemical and food and drinks spots.

PHYSICAL AND CHEMICAL PROPERTIES

PROPERTIES

Specific weight: 0.98 ± 0,01 (g/cc at 20°C)
Viscosity: (DIN 4 at 20°C) 70 ± 3
Solid content: 47% ± 1

APPLICATION METHOD

By spray and curtain coater

SPECIFICS

PREPARATION

OPU77S15G 100 parts by weight
CT23 50 parts by weight
DPU809 10-30 parts by weight.

EXPENDITURE
90-150 g/sm on one layer

DRYNG TIME

DRYING: at 20°C:
• Dust free in 25 minutes;
• Flash off in 20-35 minutes;
• Touch dry in 1 hour;
• Stackable in 12 hours   minimum.

STORAGE
Store in cool, well-ventilated places. The components react with
atmospheric moisture. Keep the partially used packaging tightly closed. The storage period is 12 months in original sealed packaging.

SUGGESTED CYCLE 
• CTE5000 series stain – 90-100 g/sqm – Alternatively TCU2000 series
• FPU15S01/CT23/DPU809 – 2:1 mixing ratio – 120-130 g/sqm
• Sanding after 8 hours
• FPU15S01/CT23NOR/DPU809 – 2:1 mixing ratio – 120-130 g/sqm
• Sanding after overnight
• OPU77S15G series/CT23NOR/DPU809 – 2:1 mixing ratio -110-130 g/sqm
• Stacking after 24 hours

 

05. PU Clear Gloss (LPU132)

Highly professional high gloss polyurethane topcoat with optimal surface hardness, very good smoothness and transparency. Specifically formulated for final buffing. Good the resistance towards yellowing.

PHYSICAL AND CHEMICAL PROPERTIES

PROPERTIES
Specific weight: 1.00 ± 0.02 g/cc at 20°C
Solid content: 57 ± 1%
Viscosity: 70’’± 5 (DIN cup 4 at 20ºC)

APPLICATION METHOD
By spray and curtain coater

SPECIFICS

PREPARATION
LPU132 100 parts by weight
CTH46 100 parts by weight
DPU809 50 parts by weight

 

DRYING TIME

DRYING at 20°C:
• Dust free in 1 hour;
• Touch dry in 3 hours;
• Stacking minimum in 48 hours.

EXPENDITURE
100-130 g/m² on one layer

STORAGE
Store in cool, well-ventilated places. The components react with atmospheric moisture. To use again the product, please close the can properly. The storage period is 12 months in original sealed packaging.

SUGGESTED CYCLE
• CTE5000 series stain – 90-100 g/sqm – Alternatively
TCU2000 series
• FPI35S06/CT20/DPU809 – 1:1 mixing ratio – 80-90 g/sqm
• PCV2019/AP2/CP2/LZC100 – 100:2:2 mixing ratio –
150-180 g/sqm
• PCV2019/AP2/CP2/LZC100- 100:2:2 mixing ratio –
150-180 g/sqm
• Sanding after overnight
• LPU132/CTH46/DPU809 – 4:1 mixing ratio – 150-160 g/sqm
• Buffing after 48-72 hours
• Stacking after 48 hours